EVALUATION OF PH CONTROL AGENTS INFLUENCING ON CORROSION OF CARBON STEEL IN SECONDARY WATER CHEMISTRY CONDITION OF PRESSURIZED WATER REACTOR

초록

The effect of various pH agents on the corrosion behavior of carbon steel was investigated under a simulated secondary water chemistry condition of a pressurized water reactor (PWR) in a laboratory, and the steel's corrosion performance was compared with the field data obtained from Uljin NPP unit 2 reactor. All tests were carried out at temperatures of 50 degrees C - 250 degrees C and pH of 8.5-10. The pH at a given temperature was controlled by adding different agents. Laboratory data indicate that the corrosion rate of carbon steel decreased as the pH increased under the test conditions and the highest corrosion rate was measured at 150 degrees C. This high corrosion rate may be related to high dissolution and instability of Fe oxide (Fe3O4) at 150 degrees C. It was also found that an addition of ethanolamine (ETA) to ammonia was more effectivefor anti-corrosion than ammonia alone, and that mixed treatment reduced 50% of iron or more at pHs of 9.5 or higher, especially in the steam generator (SG) and the moisture separator & re-heater (MSR).

키워드