Enhanced osteoconduction and angiogenesis of a three dimensional continuously porous Al2O3 implant

초록

A 3-dimensional alumina (Al2O3) implant consisting of a continuous porous structure was fabricated using a fibrous monolithic process and its biocompatibility was evaluated through in vitro procedures and in vivo angiogenesis. In vitro experiments were carried out using human osteoblast like cells, MG-63 and osteoclast-like cells, Raw-264.7. Cellular proliferation and growth behavior were examined on the specimen surfaces by SEM. Highly condensed, circular cells with three-dimensional network like growth pattern was observed inside the pore surfaces using MG-63 cells. In contrast, the osteoclast-like Raw 264.7 cells had a multi-layered pebblestone appearance with interconnections. Moreover, the crystalline-like nodules generated by osteoblasts cultured on an Al2O3 porous body were shown to have resulted from the in vitro mineralization of calcium-phosphate deposits. To investigate the in vivo angiogenesis, 3-dimensional Al2O3 porous bodies were implanted into the subcutaneous tissues of rats. The porous bodies were completely filled with fibroblasts at 4 weeks and the formation of new blood vessels inside the porous body was observed at 6 weeks. (C) 2011 Elsevier B.V. All rights reserved.

키워드